論文（Original Article）


関東育種基本区から選抜されたスギ精英樹クローンの材質

平川 泰彦・藤澤 義武・中田 了五・山下 香菜

Wood Properties of Sugi Clones Selected from Plus Trees in Kanto Breeding Region

HIRAKAWA Yasuhiko, FUJISAWA Yoshitake, NAKADA Ryogo and YAMASHITA Kana


Abstract
Wood properties of plus tree clones(the clones totaled 563 and trees 1,060 respectively) of sugi(Cryptomeria japonica) which were thirty years old and planted in the Forest Tree Breeding Center at Mito city were investigated. The grafted or cutting clones were prepared from sugi plus trees which were selected all over Kanto Breeding Region(a part of Tohoku Region, Kanto Region, Koshin Region and Tokai Region). Annual ring width, latewood percentage, basic density, moisture content of green wood, heartwood percentage, heartwood color indexes, modulus of elasticity(MOE) and modulus of rupture(MOR) in bending, tracheid length and microfibril(Mf) angle of S2 layer in tracheids were examined in samples removed from short length logs(50cm in length) at 1.8m height. Dynamic modulus of elasticity(Efr) was measured in first logs(1.8m in length). The coefficient of variation among trees was large(over 30%) in heartwood moisture content, annual ring width(outerwood), latewood percentage(outerwood) and Mf angle(outerwood), rather large in log Efr(17.5%) and MOE of small clear samples in bending(25.6%), but small(under 15%) in basic density, heartwood percentage, heartwood color indexes and tracheid length. The variation of wood properties in sugi plus tree clones reported in this study should reflect the characteristics of young plantation-grown sugi trees in Japan. It is suggested that high moisture content in heartwood and low Efr of logs which are serious problems in utilization of thinnings can be improved by tree breeding.

Key words : Sugi tree, Wood property, Plus tree clone, Plantation-grown tree

要 旨
　水戸市の旧林木育種センター育種素材保存園に植栽されていた約30年生のスギの精英樹クローン、563クローン1060個体を対象に基礎材質を調べた。供試木のクローンは、関東育種基本区（関東、甲信、東海地方及び福島県と岐阜県）に成育していた精英樹から接ぎ木または挿し木により育成されたものである。供試木の地上高約1.8m部分から約50cm長さの短尺丸太を採取し、年輪幅、晩材率、密度、生材含水率、心材率、心材色、無欠点小試験体の曲げヤング係数と曲げ強度、仮道管長および仮道管の二次壁中層のミクロフィブリル傾角を調べた。また、地際から1.8m長の丸太の動的ヤング係数を調べた。個体間の変動係数は、心材の生材含水率、外側10年輪の年輪幅、晩材率およびミクロフィブリル傾角で30％以上と特に大きく、丸太の動的ヤング係数と小試験体の曲げヤング係数では17.5％と25.6％でやや大きく、密度、心材率、心材色及び仮道管長では15％以下と小さかった。本研究で示したスギ精英樹クローンの材質変動は、日本全国におけるスギの若齢造林木のそれをほぼ表しており、スギの間伐材の利用で問題になっている心材の高含水率や丸太の低ヤング係数に関しては、育種による改良効果が期待できるものと考えられる。

キーワード：スギ、材質、精英樹クローン、造林木